Structural effects on SAPO-34 and ZIF-8 materials exposed to seawater solutions, and their potential as desalination membranes

Structural effects on SAPO-34 and ZIF-8 materials exposed to seawater solutions, and their potential as desalination membranes

Type	Journal Article
Author	Mikel C. Duke
Author	Bo Zhu
URL	http://www.sciencedirect.com/science/article/pii/S0011916415300667
Volume	377
Pages	128-137
Publication	Desalination
Date	January 1, 2016
Abstract	Researchers examined the effects of saline water on the material properties of two promising salt rejecting structures, SAPO-34 and ZIF-8, for desalination. Immersing SAPO-34 in seawater revealed a release of Al involving some replacement by Ca, K, Mg and Na. X-ray powder diffraction revealed a robust structure in deionized and seawater solutions. ZIF-8 on the other hand, lost 1% of its mass due to the release of Zn into both deionized water and seawater solutions, yet the structure remained intact. N2 and positron annihilation lifetime spectroscopy porosimetry techniques revealed loss of surface area and mesopores on both materials, explained by capillary forces acting to close them. Membrane reverse osmosis revealed no liquid water flux for SAPO-34 due to the intactness of the membrane and very small pore size which contributed to prohibitive resistance to liquid water flow. ZIF-8 membranes permeated water, but did not demonstrate significant salt rejection indicating that either the slight mass loss impacted membrane integrity to reject salt, or that liquid water diffusion in ZIF-8 does not follow a salt rejecting path. SAPO-34 and ZIF-8 structures are stable structures for aqueous applications including sea salts, but further work is needed to develop them for reverse osmosis desalination.